Aluminium Extrusion

We have Installed State of Art Extrusion & Post Process Lines including Complex Machining, cut-to-length, Ageing, Powder Coating, Anodising, Paint, and packaging on Extrusions.

• Any Sections including Pipes, Angles, Rounds, Rectangles, C Sections, Industrial, Solar, Construction, Automotive, Hardware, Heat Sinks, etc can be produced.
• Aluminium extrusion is a process by which Aluminium alloy material is forced through a die with a specific cross-sectional profile.
• A powerful ram pushes the Aluminium through the die and it emerges from the die opening.
• When it does, it comes out in the same shape as the die and is pulled out along a runout table.
• Extrusion has innumerable applications across many different industries, including architectural, automotive, electronics, aerospace, energy, and other industries.

Capacity Details

Everything Up to 6 Inch Diameter / Rectangle, 4000 Tons/PA

Extrusion

Ageing

Post Process Lines

Complex Machining 3/4/5 Axis Machining

Cut to length

Ageing

Powder Coating

Anodising

Paint

Packaging on Extrusions

Additional Facilities

Everything up to 8 inch Diameter / Rectangle,5000 Tons/PA Sublimation

Total Capacity : 9000 Tons/PA

We’ve divided the extrusion process into ten steps. Let’s take a look at what they are.

Step #1: The Extrusion Die is Prepared and Moved to the Extrusion Press

First, a round-shaped die is machined from H13 steel. Or, if one is already available, it is pulled from a warehouse like the one you see here.

Before extrusion, the die must be preheated to between 450-500 degrees Celsius to help maximize its life and ensure even metal flow.

Once the die has been preheated, it can be loaded into the extrusion press.

Step #2: An Aluminium Billet is Preheated Before Extrusion

Next, a solid, cylindrical block of Aluminium alloy, called a billet, is cut from a longer log of alloy material.

It is preheated in an oven, like this one, to between 400-500 degrees Celsius.

This makes it malleable enough for the extrusion process but not molten.

Step #3: The Billet is Transferred to the Extrusion Press

Once the billet has been preheated, it is transferred mechanically to the extrusion press.

Before it is loaded onto the press, a lubricant (or release agent) is applied to it.

The release agent is also applied to the extrusion ram, to prevent the billet and ram from sticking together.

Step #4: The Ram Pushes the Billet Material into the Container

Now, the malleable billet is loaded into the extrusion press, where the hydraulic ram applies up to 15,000 tons of pressure to it.

As the ram applies pressure, the billet material is pushed into the container of the extrusion press.

The material expands to fill the walls of the container.

Step #5: The Extruded Material Emerges Through the Die

As the alloy material fills the container, it is now being pressed up against the extrusion die.

With continual pressure being applied to it, the Aluminium material has nowhere to go except out through the opening(s) in the die.

It emerges from the die’s opening in the shape of a fully-formed profile.

Step #6: Extrusions are Guided Along the Runout Table and Quenched

After emerging, the extrusion is gripped by a puller, like the one you see here, which guides it along the runout table at a speed that matches its exit from the press.

As it moves along the runout table, the profile is “quenched,” or uniformly cooled by a water bath or by fans above the table.

Step #7: Extrusions are Sheared to Table Length

Once an extrusion reaches its full table length, it is sheared by a hot saw to separate it from the extrusion process.

At every step of the process, temperature plays an important role.

Although the extrusion was quenched after exiting the press, it has not yet fully cooled.

Step #8: Extrusions are Cooled to Room Temperature

After shearing, table-length extrusions are mechanically transferred from the runout table to a cooling table, like the one you see here.

The profiles will remain there until they reach room temperature.

Once they do, they will need to be stretched.

Step #9: Extrusions are Moved to the Stretcher and Stretched into Alignment

Some natural twisting has occurred in the profiles and this needs to be corrected.

To correct this, they are moved to a stretcher.

Each profile is mechanically gripped on both ends and pulled until it is fully straight and has been brought into specification.

Step #10: Extrusions are Moved to the Finish Saw and Cut to Length

With the table-length extrusions now straight and fully work-hardened, they are transferred to the saw table.

Here, they are sawed to pre-specified lengths, generally between 8 and 21 feet long. At this point, the properties of the extrusions match the T4 temper.

After sawing, they can be moved to an aging oven to be aged to the T5 or T6 temper.